Physical |
Test Method |
Units |
Typical Values |
Specific Gravity |
D-792 |
--- |
1.20 |
Water Absorption |
D-570 |
% |
0.32 equilibrium |
Rockwell Hardness |
D-785 |
(R Scale) |
118 |
Pencil Hardness |
D-3363 |
Scratch Hardness |
B |
Coefficient of Thermal Expansion |
D-696 |
in/in/ºF |
38 x 10-6 |
|
|
|
|
Optical |
Test Method |
Units |
Typical Values |
Light Transmission |
D-1003 |
% |
88-91 |
Refractive Index |
D-542 |
ND |
1.586 |
|
|
|
|
Mechanical |
Test Method |
Units |
Typical Values |
Tensile Strength Yield |
D-882 |
psi |
8,700 |
Tensile Strength Break |
D-882 |
psi |
10,500 |
Elongation |
D-882 |
% |
150 |
Tensile Modulus |
D-882 |
psi |
350,000 |
|
|
|
|
Thermal |
Test Method |
Units |
Typical Values |
Tensile Heat Distortion |
D-1637 |
ºF |
302º @ 50 psi |
Deflection Temperature |
D-648 |
ºF |
288º @ 264 psi |
Vicat Softening Temperature |
D-1525 |
ºF |
305-315 |
|
|
|
|
Average Properties of Rowlux® Illusion Film PETG
Physical |
Test Method |
Units |
Typical Values |
Specific Gravity |
D-792 |
--- |
1.20 |
Thermal Conductivity |
D-177 |
Btu•in/h•ft2•ºF |
1.50 |
Coefficient of Thermal Expansion |
D-696 |
mm/mm/ºC |
5.1x10-5 |
|
|
|
|
Mechanical |
Test Method |
Units |
Typical Values |
Tensile Strength Yield |
D-882 |
psi |
8,700 |
Tensile Strength Break |
D-882 |
psi |
10,500 |
Elongation at break |
D-882 |
% |
400 |
Tensile Modulus of Elasticity |
D-882 |
105 psi |
2.80 |
|
|
|
|
Thermal |
Test Method |
Units |
Typical Values |
Deflection Temperature |
D-648 |
ºF @ 264 psi |
147 |
Vicat Softening Temperature |
D-1521 |
ºF |
185 |